ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
+971 4 8809493
ESAB University Courses are incremental, structured learning modules designed to help you take your skills to the next level. New courses are being added regularly, so please check back often. Click the link to see current courses offered.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
Tips from ESAB Experts to help take your welding, cutting and fabrication skills to the next level.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
ESAB Welding Handbooks
ESAB Courses are structured learning designed to help welders achieve certain learning milestones and explore topics more in-depth. Check back often for updated resources.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
No Playlist Found ! Please Create Your PlayList Here
Visual inspection is a non-destructive testing (NDT) weld quality check process. During the testing method, the weld is examined visually through the eyes to determine surface discontinuities. The process must be conducted by an experienced welding inspector. Visual inspection of welded connections is the most common weld quality testing methods. This type of inspection is probably the most underrated and often misused, method of welding inspection. Because of its simplicity, and the absence of sophisticated equipment, the potential of this method of inspection is quite often underestimated.
Visual inspection of welding can often be the easiest to perform and is usually the least expensive to conduct.
If carried out correctly, this type of inspection can often be an extremely effective method of maintaining acceptable welding quality and preventing welding problems. There are many areas within the welding operation that can be verified and evaluated by this method of inspection. When designing an inspection plan, we need to establish the most appropriate areas to apply our inspection. We need to consider the possibility of preventing welding-related problems, rather than finding problems that may have already occurred. Non- destructive testing (NDT), which is typically used for the inspection of completed welds, is usually designed, and conducted to find welding problems after the fact when the weld is completed. Visual inspection can often be utilized to prevent welding problems from happening in the first place.
The welding inspection function is often divided into the below three areas:
We shall consider each of these inspection stages in more detail.
This inspection is conducted prior to the start of the welding operation. This type of inspection is typically associated with checking the preparation of the welding joint and verification of parameters that would be difficult or impossible to confirm during or after welding procedure. This is the area of inspection where we can best introduce controls that may prevent defective welding.
Some areas of pre-weld inspection are joint preparation inspection/pre-weld setup. This may involve the dimensional inspection of root openings. Root openings that are too tight can cause inadequate root penetration. Root openings that are too large can cause over- penetration. Groove weld bevel angles, if too small, may cause a lack of fusion. If too large, can result in distortion of the weld joint from overheating and excessive shrinkage stress.
Joint alignment (misalignment of the weld joint) can result in difficulty in producing a sound weld and stress concentration at its location, resulting in a reduction of fatigue life. Plate surface condition and cleanliness, pre-cleaning prior to welding, can often be of extreme importance. Improper or inadequate cleaning can result in unacceptable levels of porosity in the completed weld. Other pre-weld inspections may include preheat verification, temperature and heating method, presence and location of heat treatment monitoring devices, and type and efficacy of gas purging, if applicable.
Pre-weld inspection may also include evaluation and verification of documentation, material certification, filler alloy certification, welder performance qualification, welding procedure qualification, and welder and weld identification, for traceability, if applicable.
This is the inspection that is carried out during the welding operation and is concerned mainly with the requirements of the welding procedure specification (WPS). This inspection includes such items as interpass cleaning methods, interpass temperature control, welding current settings, welding travel speed, shielding gas type, gas flow rate, and welding sequence, if applicable. Also, any environmental conditions that may affect the quality of the weld such as, rain, wind, and extreme temperatures.
This inspection is typically conducted to verify the integrity of the completed weld. Many non-destructive testing (NDT) methods are used for post-weld inspection. However, even if the weld is to be subjected to NDT, it is normally wise to conduct a visual inspection first. One reason for this is surface discontinuities, which may be detected by visual inspection, can sometimes cause misinterpretation of NDT results or disguise other discontinuities within the body of the weld. The most common welding discontinuities found during the visual inspection are conditions such as undersized welds, undercut, overlap, surface cracking, surface porosity, underfill, incomplete root penetration, excessive root penetration, burn through, and excessive reinforcement.
A good pre-weld inspection plan may provide us with an excellent opportunity to prevent welding problems before they start, through the detection and correction of situations that may cause welding problems or welding discontinuities.
An inspection conducted during the welding operation can often detect problems before they escalate and also helps to provide confidence in the final welded product.
Post-weld inspection can often provide an economical method of determining a weld’s acceptability with regard to many surface discontinuities.