ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
+65 6513 9188
ESAB University Courses are incremental, structured learning modules designed to help you take your skills to the next level. New courses are being added regularly, so please check back often. Click the link to see current courses offered.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
Tips from ESAB Experts to help take your welding, cutting and fabrication skills to the next level.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
ESAB Welding Handbooks
ESAB Courses are structured learning designed to help welders achieve certain learning milestones and explore topics more in-depth. Check back often for updated resources.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
Product Stewardship and Sustainability Inquiry
No Playlist Found ! Please Create Your PlayList Here
Thin material manufacturing is a large part of the industry in the U.S. This includes various shapes of tubing, angles, and flat sheets, typically 24 gauge up to about 3/16-inch thick and usually manufactured from stainless steel, carbon steel, galvanized, or aluminum. To determine the best welding process, shielding gas, and electrode to use, start by reviewing the application. What is the base material type, thickness, condition or cleanliness, welding position, available welding equipment, and welder skill? Keep in mind the need for proper personal protective equipment, which is important when welding stainless or galvanized steel.
When welding thin material, the goal is to minimize distortion and spatter, prevent burn through, and produce a sound weld with adequate fusion.
Here are best the best practices for welding thin materials to ensure a good quality joint:
For plain carbon steel applications, you have many options. For the thinnest material up to about 14 gauge, try using the gas metal arc welding (GMAW) process in short-circuiting transfer (SCT) mode with a 0.023-inch-diameter E70-S2, S3, or S6 classification filler metal and 75 percent argon/25 percent CO2 shielding gas. On 14-gauge through 3/16-inch material, consider using a 0.030-inch-diameter filler metal.
Another potential option is to use pulsed GMAW with a high argon-content shielding gas, such as 95 percent argon/5 percent CO2 or argon/oxygen. Equipment capable of performing pulsed GMAW is more expensive but provides highly appealing benefits. Pulsed welding allows for increased control over the welding arc, offers a wide range of operating parameters, and generates low spatter.
When welding in SCT mode, you should use either a slight drag or a neutral gun angle relative to the direction of travel, which should produce a low amount of spatter. For pulsed welding, push or drag the weld puddle to determine which produces the best bead appearance. Please note that you should not back-step into the puddle, as this negates the pulse feature.
Flux-cored arc welding (FCAW) is another option, although it is not ideal because it produces a protective slag layer that needs to be removed after welding. It has lower deposition efficiency rates compared to GMAW and produces greater levels of smoke and weld spatter. Again, using a small-diameter electrode will help keep the heat input down. This process is most beneficial for job-site welding, where you can use a self-shielded, flux-cored wire. No external shielding gas is required, and most of the wires run in direct-current electrode negative, meaning most of the heat is generated in the filler metal wire and not the base material. GMAW, on the other hand, is direct-current electrode positive, which generates most of the heat in the base material.
The gas tungsten arc welding (GTAW) process works great for low-volume or high-quality welding applications. The benefits of this process include high-quality welds, no spatter, and the best fusion possible. In some cases, a filler metal is not necessary; the joint fit-up will determine this. Keep in mind, this process does require a greater degree of operator skill. To help minimize distortion, use a small tungsten electrode, such as 3/32-inch diameter, and grind it to a fine point in the direction parallel to the length of the tungsten. It is best to use 100 percent argon for shielding gas.
For some applications, you may need to use shielded metal arc welding on the joints. Be sure to choose a small-diameter electrode, use low amperage, and maintain a fast travel speed to produce an all-around good weld in the flat and horizontal positions. If you can weld only in the vertical position, increase your welding amperage by approximately 25 percent and weld in the vertical-down progression. This requires some practice, but it can produce a good weld. The more commonly used method is to weld in the vertical up position, but this isn't ideal for thin metal.
Stainless steel will use similar welding techniques and strategies as carbon steel. The preferred method is pulsed GMAW, but if SCT is the only available option, increase the inductance of the power source (if possible) to increase weld puddle control.
The main difference is matching the proper filler metal to the base metal. When welding 304 stainless steel, use a 308 filler metal and for 316 stainless, use a 316 filler metal. For welding stainless steel to carbon steel, use a 309 filler metal. The appropriate shielding gas mixtures for stainless steel GMAW are high in argon content, such as 98 percent argon/2 percent oxygen or CO2. Tri-mixes and even quad-mixes that use other gases like nitrogen or helium are available, but they are not cheap. Make sure you review your application and determine what is necessary. FCAW on stainless and carbon steel requires either 100 percent CO2 or a 75 percent argon/25 percent CO2 blend.
When welding aluminum, pre-weld joint preparation is important. All welding processes benefit from a clean weld joint, but aluminum is unique in that it has a heavy oxide layer that has a higher melting point than the base material. Preparing the joint by wire brushing or grinding off the oxide layer and using a solvent to clean it will make the welding easier and produce a cleaner weld.
The commonly used aluminum grades typically require either an ER4043/ER4047 or ER5356 filler metal. Make sure you match your filler metal to the base material. For GMAW, shielding gas blends with at least 50 percent helium and an argon balance work very well but are also expensive. If that is a concern, you can use 100 percent argon. For GTAW, use 100 percent argon and a small-diameter, 2 percent cerium tungsten electrode.
Galvanized welding will follow some of the same guidelines as welding carbon steel, except when dealing with the zinc layer on the surface, which is not conducive to the welding process and typically produces welds with porosity and poor bead appearance. If you are using GMAW, choose a shielding gas with high CO2 content, such as the 75 percent argon/25 percent CO2 blend. Carbon dioxide is an active gas, meaning it assists in the cleaning action of the weld puddle and can help prevent porosity. Additionally, using slightly higher voltage and slower travel speeds can give adequate time for the welding puddle to de-gas and for the weld toes to tie in more smoothly.
Another option is to use a smaller-diameter flux-cored wire such as a dual-shield type. This wire uses an inner flux to produce a protective slag layer, and a shielding gas to clean and protect the solidifying weld puddle. Since this process has two methods of cleaning, it may produce the best bead appearance and weld quality even though it has lower deposition efficiencies.
While we did not cover every application, scenario, or base material, this information should give you a good starting point.