OK Flux 10.72

Specifiche
Classificazioni	EN ISO 14174 : S A AB 1 57 AC H5
Omologazioni	CE : EN 13479 DB : 51.039.12 UKCA : EN 13479

Specifiche

Classificazioni

EN ISO 14174 : S A AB 1 57 AC H5

Omologazioni

CE : EN 13479
DB : 51.039.12
UKCA : EN 13479

Consumo di Flusso
34 V	1.3 kg	1.2 kg
30 V	1.0 kg	0.9 kg
26 V	0.7 kg	0.6 kg
38 V	1.6 kg	1.4 kg

Consumo di Flusso

Volt

kg flusso/ kg filo DC+

kg flusso/ kg filo AC

34 V

1.3 kg

1.2 kg

30 V

1.0 kg

0.9 kg

26 V

0.7 kg

0.6 kg

38 V

1.6 kg

1.4 kg

Classificazioni
Spoolarc 29S	A5.17:EM13K	-	-	-
OK Autrod 12.20	A5.17:EM12/ 14171-A:S2	14171-A: S 38 5 AB S2	A5.17: F7A8-EM12	A5.17: F6P8-EM12
OK Autrod 12.22	A5.17:EM12K/ 14171-A:S2Si	14171-A: S 38 5 AB S2Si	A5.17: F7A8-EM12K	A5.17: F6P8-EM12K
OK Autrod 12.24	A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo	14171-A: S 46 3 AB S2Mo	A5.23: F8A5-EA2-A3	A5.23: F8P5-EA2-A3
OK Autrod 13.24	A5.23:ENi6/ 14171-A:S3Ni1Mo0,2	-	-	-
OK Autrod 13.27	A5.23:ENi2/ 14171-A:S2Ni2	14171-A: S 46 6 AB S2Ni2	A5.23: F8A8-ENi2-Ni2	A5.23: F7P8-ENi2-Ni2
OK Autrod 13.62	A5.23:EG/ 14171-A:SZ3TiB	-	-	-
OK Autrod 13.64	A5.23:EA2TiB/ 14171-A:S2MoTiB	-	A5.23: F8TA8-EA2TiB	-

Classificazioni

filo

SFA/AWS - EN ISO

EN-come saldato

AWS-come saldato

AWS-Trattamento termico post saldatura

Spoolarc 29S

A5.17:EM13K

OK Autrod 12.20

A5.17:EM12/ 14171-A:S2

14171-A: S 38 5 AB S2

A5.17: F7A8-EM12

A5.17: F6P8-EM12

OK Autrod 12.22

A5.17:EM12K/ 14171-A:S2Si

14171-A: S 38 5 AB S2Si

A5.17: F7A8-EM12K

A5.17: F6P8-EM12K

OK Autrod 12.24

A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo

14171-A: S 46 3 AB S2Mo

A5.23: F8A5-EA2-A3

A5.23: F8P5-EA2-A3

OK Autrod 13.24

A5.23:ENi6/ 14171-A:S3Ni1Mo0,2

OK Autrod 13.27

A5.23:ENi2/ 14171-A:S2Ni2

14171-A: S 46 6 AB S2Ni2

A5.23: F8A8-ENi2-Ni2

A5.23: F7P8-ENi2-Ni2

OK Autrod 13.62

A5.23:EG/ 14171-A:SZ3TiB

OK Autrod 13.64

A5.23:EA2TiB/ 14171-A:S2MoTiB

A5.23: F8TA8-EA2TiB

Approvazioni
Spoolarc 81	-	-	-		-	-
OK Autrod 12.20				-	-	-
OK Autrod 12.22
OK Autrod 12.24				-	-	-
OK Autrod 13.27		-	-	-	-	-

Approvazioni

filo

VdTÜV

CWB

DNV

Spoolarc 81

OK Autrod 12.20

OK Autrod 12.22

OK Autrod 12.24

OK Autrod 13.27

analisi tipica del deposito
Spoolarc 29S As Welded
0.06	1.96	0.56	0.012	0.017	0.05	0.08	0.03	0.005	0.016	0.122	0.002	0.004	0.009
Spoolarc 29S Stress Relieved 1 hr. @ 1150°F
0.06	1.96	0.56	0.012	0.017	0.05	0.08	0.03	0.005	0.016	0.122	0.002	0.004	0.009
Spoolarc 75 As Welded
0.07	1.84	0.55	0.005	0.016	0.84	0.04	0.01	0.008	-	0.080	-	0.002	-
Spoolarc ENi4 As Welded
0.08	1.47	0.34	0.006	0.013	1.62	0.05	0.15	-	-	0.060	-	-	-
OK Autrod 12.20 AC, 580A, 29V
0.06	1.4	0.2	-	-	-	-	-	-	-	-	-	-	-
OK Autrod 12.20 DC+, 580A, 29V
0.05	1.5	0.2	-	-	-	-	-	-	-	-	-	-	-
OK Autrod 12.22 AC, 580A, 29V
0.06	1.4	0.3	-	-	-	-	-	-	-	-	-	-	-
OK Autrod 12.22 DC+, 580A, 29V
0.05	1.5	0.3	-	-	-	-	-	-	-	-	-	-	-
OK Autrod 12.24 AC, 580A, 29V
0.06	1.5	0.2	-	-	-	-	0.5	-	-	-	-	-	-
OK Autrod 12.24 DC+, 580A, 29V
0.05	1.6	0.2	-	-	-	-	0.5	-	-	-	-	-	-
OK Autrod 13.27 AC, 580A, 29V
0.07	1.4	0.30	-	-	2.2	-	-	-	-	-	-	-	-
OK Autrod 13.27 DC+, 520A, 29V
0.05	1.4	0.30	-	-	2.2	-	-	-	-	-	-	-	-

analisi tipica del deposito

Spoolarc 29S As Welded

0.06

1.96

0.56

0.012

0.017

0.05

0.08

0.03

0.005

0.016

0.122

0.002

0.004

0.009

Spoolarc 29S Stress Relieved 1 hr. @ 1150°F

0.06

1.96

0.56

0.012

0.017

0.05

0.08

0.03

0.005

0.016

0.122

0.002

0.004

0.009

Spoolarc 75 As Welded

0.07

1.84

0.55

0.005

0.016

0.84

0.04

0.01

0.008

0.080

0.002

Spoolarc ENi4 As Welded

0.08

1.47

0.34

0.006

0.013

1.62

0.05

0.15

0.060

OK Autrod 12.20 AC, 580A, 29V

0.06

1.4

0.2

OK Autrod 12.20 DC+, 580A, 29V

0.05

1.5

0.2

OK Autrod 12.22 AC, 580A, 29V

0.06

1.4

0.3

OK Autrod 12.22 DC+, 580A, 29V

0.05

1.5

0.3

OK Autrod 12.24 AC, 580A, 29V

0.06

1.5

0.2

0.5

OK Autrod 12.24 DC+, 580A, 29V

0.05

1.6

0.2

0.5

OK Autrod 13.27 AC, 580A, 29V

0.07

1.4

0.30

2.2

OK Autrod 13.27 DC+, 520A, 29V

0.05

1.4

0.30

2.2

Typical Wire Composition %
Spoolarc 29S
0.08	1.15	0.5	0.006	0.013	-	-	-	0.06	-	-
Spoolarc 71
0.10	1.22	0.55	0.01	0.01	-	-	-	-	0.07	-
Spoolarc 75
0.08	0.89	0.46	0.01	0.00	0.98	0.04	0.01	0.07	-	-
Spoolarc 81
0.09	0.95	0.26	0.01	0.01	-	-	-	-	-	-
Spoolarc ENi4
0.17	0.73	0.19	0.00	0.00	1.74	-	0.17	0.06	-	-
OK Autrod 12.20
0.10	1.06	0.07	-	-	-	-	-	-	-	-
OK Autrod 12.22
0.09	1.01	0.19	-	-	-	-	-	-	-	-
OK Autrod 12.24
0.09	1.08	0.14	-	-	-	-	0.48	-	-	-
OK Autrod 13.24
0.12	1.52	0.23	-	-	0.88	-	0.19	-	-	-
OK Autrod 13.27
0.10	1.02	0.14	-	-	2.19	-	-	-	-	-
OK Autrod 13.62
0.07	1.55	0.28	-	-	-	-	0.01	-	0.14	0.013
OK Autrod 13.64
0.07	1.22	0.28	-	-	-	-	0.49	-	0.14	0.013

Typical Wire Composition %

Spoolarc 29S

0.08

1.15

0.5

0.006

0.013

0.06

Spoolarc 71

0.10

1.22

0.55

0.01

0.07

Spoolarc 75

0.08

0.89

0.46

0.01

0.00

0.98

0.04

0.01

0.07

Spoolarc 81

0.09

0.95

0.26

0.01

Spoolarc ENi4

0.17

0.73

0.19

0.00

1.74

0.17

0.06

OK Autrod 12.20

0.10

1.06

0.07

OK Autrod 12.22

0.09

1.01

0.19

OK Autrod 12.24

0.09

1.08

0.14

0.48

OK Autrod 13.24

0.12

1.52

0.23

0.88

0.19

OK Autrod 13.27

0.10

1.02

0.14

2.19

OK Autrod 13.62

0.07

1.55

0.28

0.01

0.14

0.013

OK Autrod 13.64

0.07

1.22

0.28

0.49

0.14

0.013

Proprietà meccaniche tipiche
Spoolarc 29S	Come saldato	532 MPa	622 MPa	25 %	57 J @ -40 °C 43 J @ -46 °C 41 J @ -51 °C
Spoolarc 75	Come saldato	556 MPa	646 MPa	28 %	91 J @ -40 °C 83 J @ -51 °C
Spoolarc 81	Come saldato	415 MPa	500 MPa	30 %	119 J @ -29 °C 100 J @ -40 °C 71 J @ -51 °C 50 J @ -62 °C
Spoolarc ENi4	Come saldato	607 MPa	677 MPa	27 %	141 J @ -40 °C 107 J @ -51 °C 88 J @ -62 °C
OK Autrod 12.20	Come saldato AWS DC+	415 MPa	500 MPa	30 %	125 J @ -30 °C 100 J @ -40 °C 70 J @ -50 °C 50 J @ -62 °C
OK Autrod 12.20	Come saldato EN AC	420 MPa	500 MPa	33 %	140 J @ -30 °C 130 J @ -40 °C 80 J @ -50 °C
OK Autrod 12.22	Come saldato EN AC	425 MPa	500 MPa	32 %	140 J @ -30 °C 130 J @ -40 °C 80 J @ -50 °C
OK Autrod 12.22	Come saldato AWS DC+	415 MPa	500 MPa	30 %	120 J @ -30 °C 100 J @ -40 °C 70 J @ -50 °C 50 J @ -62 °C
OK Autrod 12.24	Come saldato AWS DC+	500 MPa	590 MPa	25 %	60 J @ -30 °C 40 J @ -40 °C 35 J @ -46 °C
OK Autrod 12.24	Come saldato EN AC	535 MPa	600 MPa	24 %	70 J @ -30 °C 50 J @ -40 °C 40 J @ -50 °C
OK Autrod 13.24	Come saldato AWS DC+	530 MPa	660 MPa	28 %	90 J @ 0 °C 35 J @ -40 °C
OK Autrod 13.27	Come saldato EN AC	520 MPa	610 MPa	27 %	120 J @ -30 °C 100 J @ -40 °C 80 J @ -50 °C 60 J @ -60 °C
OK Autrod 13.27	Come saldato AWS DC+	490 MPa	610 MPa	30 %	100 J @ -40 °C 80 J @ -51 °C 50 J @ -62 °C
OK Autrod 13.62	Come saldato (acc. AWS) Plate thickness: 12mm; Heat Input: 2.2kJ/mm; Side 1: 600A, 32V, 53cm/min; Side 2: 700A, 32V, 60cm/min; DC+	500 MPa	610 MPa	27 %	50 J @ -62 °C
OK Autrod 13.64	Come saldato (acc. to AWS) Plate thickness 12mm Heat input 2.2kJ/mm 700A, 32V, 60cm/min DC+	560 MPa	660 MPa	27 %	50 J @ -62 °C

Proprietà meccaniche tipiche

filo

Stato

Resistenza allo snervamento

Resistenza alla trazione

Allungamento

Intaglio a V Charpy

Spoolarc 29S

Come saldato

532 MPa

622 MPa

25 %

57 J @ -40 °C
43 J @ -46 °C
41 J @ -51 °C

Spoolarc 75

Come saldato

556 MPa

646 MPa

28 %

91 J @ -40 °C
83 J @ -51 °C

Spoolarc 81

Come saldato

415 MPa

500 MPa

30 %

119 J @ -29 °C
100 J @ -40 °C
71 J @ -51 °C
50 J @ -62 °C

Spoolarc ENi4

Come saldato

607 MPa

677 MPa

27 %

141 J @ -40 °C
107 J @ -51 °C
88 J @ -62 °C

OK Autrod 12.20

Come saldato AWS DC+

415 MPa

500 MPa

30 %

125 J @ -30 °C
100 J @ -40 °C
70 J @ -50 °C
50 J @ -62 °C

OK Autrod 12.20

Come saldato EN AC

420 MPa

500 MPa

33 %

140 J @ -30 °C
130 J @ -40 °C
80 J @ -50 °C

OK Autrod 12.22

Come saldato EN AC

425 MPa

500 MPa

32 %

140 J @ -30 °C
130 J @ -40 °C
80 J @ -50 °C

OK Autrod 12.22

Come saldato AWS DC+

415 MPa

500 MPa

30 %

120 J @ -30 °C
100 J @ -40 °C
70 J @ -50 °C
50 J @ -62 °C

OK Autrod 12.24

Come saldato AWS DC+

500 MPa

590 MPa

25 %

60 J @ -30 °C
40 J @ -40 °C
35 J @ -46 °C

OK Autrod 12.24

Come saldato EN AC

535 MPa

600 MPa

24 %

70 J @ -30 °C
50 J @ -40 °C
40 J @ -50 °C

OK Autrod 13.24

Come saldato AWS DC+

530 MPa

660 MPa

28 %

90 J @ 0 °C
35 J @ -40 °C

OK Autrod 13.27

Come saldato EN AC

520 MPa

610 MPa

27 %

120 J @ -30 °C
100 J @ -40 °C
80 J @ -50 °C
60 J @ -60 °C

OK Autrod 13.27

Come saldato AWS DC+

490 MPa

610 MPa

30 %

100 J @ -40 °C
80 J @ -51 °C
50 J @ -62 °C

OK Autrod 13.62

Come saldato (acc. AWS) Plate thickness: 12mm; Heat Input: 2.2kJ/mm; Side 1: 600A, 32V, 53cm/min; Side 2: 700A, 32V, 60cm/min; DC+

500 MPa

610 MPa

27 %

50 J @ -62 °C

OK Autrod 13.64

Come saldato (acc. to AWS) Plate thickness 12mm Heat input 2.2kJ/mm 700A, 32V, 60cm/min DC+

560 MPa

660 MPa

27 %

50 J @ -62 °C

Ordini

Descrizione

Codice prodotto

Codice prodotto: 1072800P00

Codice prodotto: 1072800P0W

Codice prodotto: 1072H00P0W

Codice prodotto: 1072Y00P00

Idrogeno diffusibile	max 5 ml H/100g weld metal (Redried flux)
Tipo di scoria	Aluminate-basic
Trasferimento lega	No Silicon and moderately Manganese alloying
Densità	nom: 1.2 kg/dm3
Indice di basicità	nom: 1.9

Ricerca prodotti

Accessori per consumabili

Accessori per saldatrici

Consumabili per torce MIG

Forniture generiche

Aspirazione fumi

Mani e corpo

Teste e volto

Acciaio al carbonio

Acciaio inossidabile

Alluminio

Altro

Basso legati

Nickel

Rame

Riporti duri

Impianti robot

Monitoraggio dati di saldatura

Programma

Monitoraggio dati di saldatura

Programma

Saldatrici a batteria

Saldatrici elettrodo

Saldatrici MIG-MAG

Saldatrici multiprocesso

Saldatrici TIG

Unità trainafilo

Arco sommerso

Monitoraggio dati di saldatura

Saldatura meccanizzata

Elettrodi al carbone per scriccatura

Taglio esotermico

Torcia per scriccatura

Accessori

Controlli CNC

Macchine da taglio

Machine plasma

Programma

Torce ossitaglio

Torce MIG

Torce per scriccatura

Torce plasma

Torce TIG

OK Flux 10.72

Specifiche

Ordini

Documenti

Schede tecniche

Documenti aggiuntivi

Hai bisogno di supporto sui prodotti?

Informazione e supporto proditti